前言：德国巴斯夫塑胶原料代理,德国巴斯夫TPU代理商,巴斯夫1190A10代理,TPU1190A10原料,1190A10原厂原包
供应TPU 德国巴斯夫塑胶原料代理商 1190A10 注塑级-宣传视频
机械性能额定值单位制测试方法：-20°C 186 MPa ISO 6721-1,-4 20°C 51.0 MPa ISO 6721-1,-4 60°C 37.0 MPa ISO 6721-1,-4 抗磨损性 (23°C) 30.0 mm? ISO 4649-ATPU1190A10 注塑级物性表物理性能测试条件测试方法测试结果单位熔体质量流动速率190°C/10.0kgASTMD123810to20g/10min190°C/21.6kgASTMD123810to40g/10min机械性能测试条件测试方法测试结果单位拉伸模量ASTM D-63831Mpa弯曲模量ASTM D-79044.8Mpa100％拉伸应力ASTM D-41210.3Mpa300％拉伸应力ASTM D-41217.2Mpa断裂拉伸强度ASTM D-41236.5Mpa伸长率断裂ASTM D-412580%撕裂强度ASTM D-624130kN/m硬度shoreAASTM D-224091拉伸模量注塑ASTMD41231.0Mpa弯曲模量注塑ASTMD79029.0Mpa泰伯耐磨性ASTMD104445.0mgAbrasion-DINDIN5351625mm?热性能测试条件测试方法测试结果单位玻璃转化温度内部方法-35.0°C维卡软化温度ASTMD1525120°CSofteningPoint-DMA内部方法100°C弹性体测试条件测试方法测试结果单位拉伸应力****应变ASTMD41212.4Mpa300%应变ASTMD41227.6Mpa抗张强度ASTMD41237.2Mpa伸长率断裂ASTMD412460%撕裂强度2ASTMD624128kN/m压缩yongjiu变形23°C,22hrASTMD395B25%70°C,22hrASTMD395B45%硬度测试条件测试方法测试结果单位肖氏硬度邵氏AASTMD224090基本性能测试条件测试方法测试结果单位密度ASTM D-7921.13g/cm